Part number | 992008KR | |
---|
EAN | 8716106060924 | |
---|
Unit | Each | |
---|
Details | Zinc content approx. 90% | |
---|
Application range | - For large surfaces that have not yet been painted
- For the repair of damaged galvanised parts, corrosion protection for weld seams, and the cold galvanisation of metal surfaces in mechanical engineering, plant engineering and bodywork
| |
---|
Properties | - Can be painted with synthetic resin paint
- Cannot be painted with 2K paints
- Theoretical yield: 8 m²/l or 3.4 m² with a coat thickness of 50 µm
- Apply using a brush or roller
- Ventilation time: at least 10 minutes before any oven drying
- Quick drying
- Temperature-resistant to approx. 400°C
- Colour: matt
- Specific weight: 2.16–2.30 kg/l
- Chromate-free and lead-free
| |
---|
Technical info | - Processing temperature: +5 to +30°C air and object temperature; take note of dew point
- Pre-treatment of iron and steel surfaces: sand blasting
- Dust-dry after 20–30 minutes (at 20°C)
- Set to touch after 50–60 minutes (at 20°C)
- Hardened after 6 hours (at 20°C)
- Can be coated after 12 hours (at 20°C)
- Final hardness after 3–4 days (at 20°C)
- Lower temperatures result in longer drying times
- The thickness of the applied layer must not exceed 150 µm per pass
| |
---|
Benefits | Corrosion protection with a high level of protection for iron and steel | |
---|
Brand colour | n/a | |
---|
Base colour | Grey | |
---|
Base medium | Synthetic resin | |
---|
Designed for material | Metal | |
---|
Category | Vehicle/car paint | |
---|
Packing type | Tin | |
---|
Additional info | *Please note that this item is either a dangerous good or a non-standard delivery size. This means a specialist carrier will be used and this item will take upto 48 hours to deliver. | |
---|