Details | - Active corrosion protection (zinc phosphate)
- Quick drying (lower temperatures lead to a longer drying time)
- High coverage
- Chromate-free and lead-free
- High filling capability
| |
---|
Application range | - Suitable for iron and steel
- Can also be applied as a thick layer
- For electrostatic discharge
- Can be coated with 1K and 2K paints
| |
---|
Properties | - Basic binding agent: acrylic resin
- Adhesion (DIN 53 151): iron, steel: class 0 (very good)
- Outside storage for a maximum of 5 days without final coating
- Dust dry after 15 - 20 minutes, touchable after 45 - 60 minutes, cured after 4 - 5 hours and final hardness after 3 - 4 days (at 20°C)
| |
---|
Technical info | - Processing conditions: at + 10°C and a maximum relative humidity of 80%
- The drying time can be accelerated by diluting the base colour with a quick-drying agent instead of a synthetic resin
- Theoretical coating with a thickness of 50 µm
| |
---|
Benefits | - Long service life
- Saves time
- Economical
- Less polluting
- Smooth surface
| |
---|